The crack initiates at stress concentration point in the root of weld, where has much more martenite, carbide and inclusion, and the serious hydrogen segregation.

裂纹均在焊缝根部应处萌生，该处马氏含量比较大，碳化杂较多，氢的偏聚现象严重。